| 詳細參數 | |||
|---|---|---|---|
| 品牌/廠家 | Braskem | 類型 | 正牌料 |
| 用途級別 | 薄膜級 | 加工級別 | 擠出級 |
| 特性級別 | 耐低溫 | 外觀顏色 | 白色 |
| 密度 | 0.935g/cm3 | 拉伸強度 | 50kg |
| 彎曲強度 | 48kg | 缺口沖擊強度 | 9kg.cm |
| 斷裂伸長率 | 800% | 成型收縮率 | 72% |
| 熔體流動速率 | 0.50g/10min | ||
Braskem EVA TN2005
乙烯醋酸乙烯共聚物
Braskem
產品說明:
TN2005 is an Ethylene-Vinyl Acetate (EVA) copolymer with high molecular weight, excellent mechanical properties, transparency, high gloss and easy processability. Additionally, TN2005 has flexibility even at low temperatures and good sealing properties. TN2005 can be used as base polymer for the manufacture of greenhouse films with excellent thermal properties. More detailed inbation about agricultural film applications and light stabilization recommendations, please contact a Braskem representative.
Application:
|
|
||||
|
|
||||
|
總體 |
|
|||
|
材料狀態(tài) |
|
|||
|
添加劑 |
|
|||
|
特性 |
|
|||
|
用途 |
|
|||
|
機構評級 |
|
|||
|
加工方法 |
|
|||
|
物理性能 |
額定值 |
單位制 |
測試方法 |
|
密度 |
0.935 |
g/cm3 |
ASTM D1505 |
|
熔流率（熔體流動速率） (190°C/2.16 kg) |
0.50 |
g/10 min |
ASTM D1238 |
|
醋酸乙烯含量 |
13.5 |
wt% |
|
|
硬度 |
額定值 |
單位制 |
測試方法 |
|
肖氏硬度 |
|
|
ASTM D2240 |
|
邵氏 A, 模壓成型 |
91 |
|
|
|
邵氏 D, 模壓成型 |
50 |
|
|
|
機械性能 |
額定值 |
單位制 |
測試方法 |
|
抗張強度 (斷裂, 模壓成型) |
3630 |
psi |
ASTM D638 |
|
伸長率 (斷裂, 模壓成型) |
680 |
% |
ASTM D638 |
|
薄膜 |
額定值 |
單位制 |
測試方法 |
|
薄膜厚度 - 經測試 |
2.0 |
mil |
|
|
割線模量 |
|
|
ASTM D882 |
|
2% 正割, MD : 2.0 mil, 吹塑薄膜 |
8700 |
psi |
|
|
2% 正割, TD : 2.0 mil, 吹塑薄膜 |
10200 |
psi |
|
|
抗張強度 |
|
|
ASTM D882 |
|
MD : 斷裂, 2.0 mil, 吹塑薄膜 |
4350 |
psi |
|
|
TD : 斷裂, 2.0 mil, 吹塑薄膜 |
4930 |
psi |
|
|
伸長率 |
|
|
ASTM D882 |
|
MD : 斷裂, 2.0 mil, 吹塑薄膜 |
400 |
% |
|
|
TD : 斷裂, 2.0 mil, 吹塑薄膜 |
800 |
% |
|
|
落錘沖擊 (2.0 mil, 吹塑薄膜) |
430 |
g |
ASTM D1709B |
|
埃爾曼多夫抗撕強度 |
|
|
ASTM D1922 |
|
MD : 2.0 mil, 吹塑薄膜 |
100 |
g |
|
|
TD : 2.0 mil, 吹塑薄膜 |
270 |
g |
|
|
熱性能 |
額定值 |
單位制 |
測試方法 |
|
維卡軟化溫度 |
167 |
°F |
ASTM D1525 2 |
|
熔融峰值溫度 |
|
|
|