| 詳細參數(shù) | |||
|---|---|---|---|
| 品牌/廠家 | 美國液氮 | 牌號 | R10002E |
| 類型 | 正牌料 | 加工級別 | 注射級 |
| 熔體流動速率 | 1g | 密度 | 1.24g |
| 拉伸強度 | 7kg | 彎曲強度 | 4kg |
| 彎曲模量 | 5kg | 缺口沖擊強度 | 6kg.cm |
| 斷裂伸長率 | 65% | 成型收縮率 | 1% |
| 熱變形溫度 | 255℃ | 吸水率 | 1.2% |
| 特性級別 | 熱穩(wěn)定性 抗化學性 阻燃級 增韌級 耐低溫 耐水解 高抗沖 高滑動 耐磨 | 用途級別 | 電子電器部件 汽車部件 家電部件 |
| 產(chǎn)地 | 美國 | ||
無鹵防火聚酰胺66/6 Starflam R10002E
PA66 基礎(chǔ)創(chuàng)新塑料(美國) R10002E-BK1B568
無鹵無磷阻燃 ROHS合規(guī) (R1000Z220EM)
Eurostar Starflam R10002E PA66/6, Injection Molded
Starflam R10002E是一個非填充，無鹵素和無紅磷的阻燃的聚酰胺66/聚酰胺6注塑樹脂（又稱R1000Z220EM ）
物理性能：
| Density | 1.17 g/cc | 0.0423 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00800 - 0.0150 cm/cm | 0.00800 - 0.0150 in/in | on Tensile Bar; ISO 294 |
熱性能：
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
UL RTI, Electrical 
|
65.0 °C @Thickness 0.400 mm |
149 °F @Thickness 0.0157 in |
|
|
120 °C @Thickness 0.800 mm |
248 °F @Thickness 0.0315 in |
||
|
120 °C @Thickness 1.60 mm |
248 °F @Thickness 0.0630 in |
||
|
120 °C @Thickness 3.00 mm |
248 °F @Thickness 0.118 in |
||
|
UL RTI, Mechanical with Impact
|
65.0 °C @Thickness 0.400 mm |
149 °F @Thickness 0.0157 in |
|
|
65.0 °C @Thickness 0.800 mm |
149 °F @Thickness 0.0315 in |
||
|
75.0 °C @Thickness 1.60 mm |
167 °F @Thickness 0.0630 in |
||
|
75.0 °C @Thickness 3.00 mm |
167 °F @Thickness 0.118 in |
||
|
UL RTI, Mechanical without Impact
|
65.0 °C @Thickness 0.400 mm |
149 °F @Thickness 0.0157 in |
|
|
85.0 °C @Thickness 0.800 mm |
185 °F @Thickness 0.0315 in |
||
|
85.0 °C @Thickness 1.60 mm |
185 °F @Thickness 0.0630 in |
||
|
85.0 °C @Thickness 3.00 mm |
185 °F @Thickness 0.118 in |
||
|
Flammability, UL94
|
V-0 @Thickness 0.400 mm |
V-0 @Thickness 0.0157 in |
IEC 60695-11-10 |
|
V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
IEC 60695-11-10 | |
|
V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
IEC 60695-11-10 | |
|
V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
IEC 60695-11-10 | |