性能特點：礦物填料17%增強,無溴 阻燃,尺寸穩(wěn)定.PPE+PS
PPE + PS混合。17%的礦物增強。Non-brominated non-chlorinated FR系統(tǒng)。阻燃UL94 V0 / 5VA 等級。UL746C f1。絕緣強度。尺寸穩(wěn)定性。適合市場E / E室內(nèi)/室外的應(yīng)用包括電氣天花板盒和煙霧探測器。
物性數(shù)據(jù)：
溶指7.6，收縮率0.5-0.7%，沖擊強度130J/M，熱變形溫度108-128℃，維卡軟化溫度132-136℃，表面電阻率>1.0E+16ohm，體積電阻率1.2E+16ohm.cm，加工熔體溫度282-310℃。
| TYPICAL PROPERTIES (1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, yld, Type I, 5 mm/min | 750 | kgf/cm2 | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 610 | kgf/cm2 | ASTM D 638 | |
| Tensile Strain, yield | 3.8 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 8.4 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 37200 | kgf/cm2 | ASTM D 638 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 1190 | kgf/cm2 | ASTM D 790 | |
| Flexural Stress, yld, 2.6 mm/min, 100 mm span | 1190 | kgf/cm2 | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 37400 | kgf/cm2 | ASTM D 790 | |
| Flexural Modulus, 2.6 mm/min, 100 mm span | 36200 | kgf/cm2 | ASTM D 790 | |
| Tensile Stress, yield | 71 | MPa | ISO 527 | |
| Tensile Stress, break | 57 | MPa | ISO 527 | |
| Tensile Strain, yield | 3.7 | % | ISO 527 | |
| Tensile Strain, break | 10.5 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 4000 | MPa | ISO 527 | |
| Flexural Stress | 117 | MPa | ISO 178 | |
| Flexural Modulus | 3800 | MPa | ISO 178 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, unnotched, 23°C | 227 | cm-kgf/cm | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 13 | cm-kgf/cm | ASTM D 256 | |
| Izod Impact, Reverse Notched, 3.2 mm | 82 | cm-kgf/cm | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 4517 | cm-kgf | ASTM D 3763 | |
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m2 | ISO 180/1A | |
| Charpy Impact, notched, 23°C | 10 | kJ/m2 | ISO 179/2C | |
| THERMAL | Value | Unit | Standard | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 117 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 108 | °C | ASTM D 648 | |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 128 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 116 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 7.06E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 7.76E-05 | 1/°C | ASTM E 831 | |
| Vicat Softening Temp, Rate B/50 | 132 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 136 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 126 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 111 | °C | ISO 75/Ae | |
| Relative Temp Index, Elec | 100 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 85 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 100 | °C | UL 746B | |
| PHYSICAL | Value | Unit | Standard | |
| Specific Gravity | 1.25 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.5 - 0.7 | % | SABIC Method | |
| Melt Flow Rate, 280°C/5.0 kgf | 7.6 | g/10 min | ASTM D 1238 | |
| Melt Flow Rate, 300°C/5.0 kgf | 7.6 | g/10 min | ASTM D 1238 | |
| Melt Volume Rate, MVR at 280°C/5.0 kg | 6 | cm3/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 300°C/5.0 kg | 6 | cm3/10 min | ISO 1133 | |
| ELECTRICAL | Value | Unit | Standard | |
| Volume Resistivity | 1.2E+16 | Ohm-cm | ASTM D 257 | |
| Surface Resistivity | >1.E+16 | Ohm | ASTM D 257 | |
| Dielectric Strength, in oil, 3.2 mm | 17.3 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 50/60 Hz | 2.89 | - | ASTM D 150 | |
| Relative Permittivity, 1 MHz | 2.7 | - | ASTM D 150 | |
| Dissipation Factor, 50/60 Hz | 0.017 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.0044 | - | ASTM D 150 | |
| Arc Resistance, Tungsten {PLC} | 6 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 0 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 3 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 2 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A | |
| FLAME CHARACTERISTICS | Value | Unit | Standard | |
| UL Recognized, 94V-0 Flame Class Rating (3) | 1.47 | mm | UL 94 | |
| UL Recognized, 94-5VA Rating (3) | 2 | mm | UL 94 | |
| Radiant Panel Listing | YES | - | UL Tested | |
| UV-light, water exposure/immersion | F1 | - | UL 746C | |