可發(fā)泡性PPO NORYL Resin FN215X
PPO 基礎創(chuàng)新塑料(美國) FN215X-780
NORYL Resin FN215X
性能特點：PPE+PS，可發(fā)泡性。結(jié)構(gòu)性泡沫樹脂。
加工方法:泡沫處理。
物性數(shù)據(jù)：
收縮率0.6-0.8%，沖擊強度200J/M，熱變形溫度76.7-88.9℃，表面電阻率>1.0E+17ohm，阻燃V-0。
| TYPICAL PROPERTIES (1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| FOAM - MECHANICAL 6.4 mm Wt Reduction | 20 | % | - | |
| Tensile Stress, yield, 6.35 mm | 290 | kgf/cm2 | ASTM D 638 | |
| Tensile Strain, break, 6.35 mm | 12 | % | ASTM D 638 | |
| Flexural Stress, yield, 6.4 mm | 620 | kgf/cm2 | ASTM D 790 | |
| Flexural Modulus, 6.4 mm | 19400 | kgf/cm2 | ASTM D 790 | |
| IMPACT | Value | Unit | Standard | |
| FOAM - IMPACT 6.4 mm Wt Reduction | 20 | % | - | |
| Izod Impact, unnotched, 23°C, 6.4mm | 20 | cm-kgf/cm | ASTM D 4812 | |
| Instrumented Impact Energy @ peak, 23°C | 111 | cm-kgf | ASTM D 3763 | |
| Instrumented Impact Energy @ peak, -30 | 33 | cm-kgf | ASTM D 3763 | |
| THERMAL | Value | Unit | Standard | |
| FOAM - THERMAL 6.4mm Wt Reduction | 20 | % | - | |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 88 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 76 | °C | ASTM D 648 | |
| Relative Temp Index, Elec | 85 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 85 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 85 | °C | UL 746B | |
| PHYSICAL | Value | Unit | Standard | |
| FOAM - PHYSICAL 6.4mm Wt Reduction | 20 | % | - | |
| Specific Gravity | 1.1 | - | ASTM D 792 | |
| Specific Gravity, foam molded | 0.88 | - | ASTM D 792 | |
| Water Absorption, 24 hours | 0.07 | % | ASTM D 570 | |
| Water Absorption, equilibrium, 23C | 0.17 | % | ASTM D 570 | |
| Mold Shrinkage, flow, 6.4 mm (5) | 0.6 - 0.8 | % | SABIC Method | |
| ELECTRICAL | Value | Unit | Standard | |
| Surface Resistivity | >1.E+17 | Ohm | ASTM D 257 | |
| Dielectric Strength, in oil, 1.6 mm | 12 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 1 MHz | 2.2 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.0044 | - | ASTM D 150 | |
| Arc Resistance, Tungsten {PLC} | 6 | PLC Code | ASTM D 495 | |
| High Voltage Arc Track Rate {PLC} | 4 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 1 | PLC Code | UL 746A | |
| FLAME CHARACTERISTICS | Value | Unit | Standard | |
| FOAM - Flame Class Minimum Density | 0.85 | g/cm3 | - | |
| UL Recognized, 94V-1 Flame Class Rating (3) | 2.99 | mm | UL 94 | |
| UL Recognized, 94V-0 Flame Class Rating (3) | 5.99 | mm | UL 94 | |
| UL Recognized, 94-5VA Rating (3) | 3.91 | mm | UL 94 | |
| Radiant Panel Listing | YES | - | UL Tested | |
| UV-light, water exposure/immersion | F1 | - | UL 746C | |