產(chǎn)品參數(shù)
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 物理性能 | 成型收縮率 | ASTM D-955 | 0.9-1.4 | % | |
| 比重 | ASTM D-792 | 1.06 | |||
| 機械性能 | 彎曲模量 | ASTM 790 | 2840 | MPa | |
| Izod缺口沖擊強度 | ASTM D-256 | 50 | J/m | ||
| Izod缺口沖擊強度 | ASTM D-256 | 5 | Kg.cm/cm | ||
| 彎曲強度 | ASTM D-790 | 7700 | psi | ||
| 彎曲模量 | ASTM D-790 | 29000 | Kg/cm2 | ||
| 彎曲強度 | ASTM D-790 | 33 | MPa | ||
| 拉伸屈服強度 | ASTM D-638 | 5300 | psi | ||
| 拉伸屈服強度 | ASTM D-638 | 36 | MPa | ||
| 斷裂伸長率 | ASTM D-638 | 20 | % | ||
| 彎曲強度 | ASTM D-790 | 540 | Kg/cm2 | ||
| 拉伸屈服強度 | ASTM D-638 | 370 | Kg/cm2 | ||
| Izod缺口沖擊強度 | ASTM D-256 | 0.9 | ft.lb/in | ||
| 彎曲模量 | ASTM D-790 | 410 | psi | ||
| 熱性能 | 熱變形溫度 | 0.45Mpa | ASTM D-648 | 145 | ℃ |
| 熱變形溫度 | 1.82Mpa | ASTM D-648 | 200 | °F | |
| 熱變形溫度 | 0.45Mpa | ASTM D-648 | 295 | °F | |
| 耐燃性 | ASTM UL94 | HB | class | ||
| 熱變形溫度 | 1.82Mpa | ASTM D-648 | 92 | ℃ | |