產(chǎn)品參數(shù)
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
| 基本性能 | 熔體流動速率 | 200℃ 21.6kg | 錦湖方法 | 50 | g/10min | |
| 熔體流動速率 | 200℃ 5kg | ASTM D-1238 | 4.5 | g/10min | ||
| 物理性能 | 比重 | 23/23℃ | ASTM D-792 | 1.04 | ||
| 模塑收縮率 | ASTM D-955 | 0.4-0.7 | % | |||
| 機(jī)械性能 | 拉伸強(qiáng)度 | 23℃ | ASTM D-638 | 480(6800) | kg/cm2(psi) | |
| 彎曲模量 | 23℃ | ASTM D-790 | 24000(340000) | kg/cm2(psi) | ||
| 彎曲強(qiáng)度 | 23℃ | ASTM D-790 | 650(9300) | kg/cm2(psi) | ||
| IZOD沖擊強(qiáng)度 | 1/4in(6.4mm) 23℃ | ASTM D-256 | 23(4.2) | kg.cm/cm(ft.ld/in) | ||
| 彎曲模量 | 23℃ | ASTM D-790 | 24000(340000) | kg/cm2(psi) | ||
| IZOD沖擊強(qiáng)度 | 1/8in(3.2mm) 23℃ | ASTM D-256 | 26(4.7) | kg.cm/cm(ft.ld/in) | ||
| 伸長率 | ASTM D-638 | 30 | % | |||
| 熱性能 | 阻燃性 | UL-94 | HB | |||
| 維卡軟化點(diǎn) | ASTM D-1525 | 95(203) | ℃(℉) | |||
| 熱變形溫度 | 未退火 | 6.4mm 18.6kg/cm2 | ASTM D-648 | 85(185) | ℃(℉) | |
| 退火 | 6.4mm 18.6kg/cm2 | ASTM D-648 | 95(203) | ℃(℉) | ||
| 其它性能 | 食品衛(wèi)生性 | 適合 | ||||