| 特性 | 抗撞擊性，高 耐熱性，高 |
| 加工方法 | 注射成型 |
| 多點數(shù)據(jù) | Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Compressive Stress vs. Strain (ASTM D695) Flexural DMA (ASTM D4065) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Creep (ASTM D2990) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835) |
| 密度 | 1.22 | g/cm3 | ISO 1183 |
| 溶化體積流率（MVR）(265°C/5.0 kg) | 10.0 | cm3/10min | ISO 1133 |
| 收縮率 - 流動(3.20 mm) | 0.40 到 0.60 | % | 內(nèi)部方法 |
| 吸水率 | ISO 62 | ||
| 飽和, 23°C | 0.40 | % | ISO 62 |
| 平衡, 23°C, 50% RH | 0.10 | % | ISO 62 |
| 拉伸模量 | 3200 | MPa | ISO 527-2/1 |
| 拉伸應(yīng)力 | ISO 527-2/5 | ||
| 屈服 | 55.0 | MPa | ISO 527-2/5 |
| 斷裂 | 58.0 | MPa | ISO 527-2/5 |
| 拉伸應(yīng)變 | ISO 527-2/5 | ||
| 屈服 | 4.2 | % | ISO 527-2/5 |
| 斷裂 | 100 | % | ISO 527-2/5 |
| 彎曲模量1 | 3100 | MPa | ISO 178 |
| 彎曲應(yīng)力 | 95.0 | MPa | ISO 178 |
| 簡支梁缺口沖擊強度2(23°C) | 35 | kJ/m2 | ISO 179/1eA |
| 懸壁梁缺口沖擊強度3 | ISO 180/1A | ||
| -30°C | 10 | kJ/m2 | ISO 180/1A |
| 23°C | 30 | kJ/m2 | ISO 180/1A |
| 熱變形溫度4(1.8 MPa, 未退火, 64.0 mm跨距) | 118 | °C | ISO 75-2/Af |
| 維卡軟化溫度 | |||
| -- | 135 | °C | ISO 306/B50 |
| -- | 137 | °C | ISO 306/B120 |
| 線形熱膨脹系數(shù) | ISO 11359-2 | ||
| 流動 : -40 到 40°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| 橫向 : -40 到 40°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| 干燥溫度 | 110 到 121 | °C | |
| 干燥時間 | 3.0 到 4.0 | hr | |
| 干燥時間，大 | 8.0 | hr | |
| 建議的大水分含量 | 0.040 | % | |
| 建議注射量 | 30 到 80 | % | |
| 料筒后部溫度 | 260 到 271 | °C | |
| 料筒中部溫度 | 266 到 288 | °C | |
| 料筒前部溫度 | 271 到 299 | °C | |
| 射嘴溫度 | 271 到 299 | °C | |
| 加工（熔體）溫度 | 282 到 299 | °C | |
| 模具溫度 | 77 到 99 | °C | |
| 背壓 | 0.345 到 0.689 | MPa | |
| 螺桿轉(zhuǎn)速 | 40 到 70 | rpm | |
| 排氣孔深度 | 0.038 到 0.076 | mm |