產(chǎn)品參數(shù)
| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 吸水率 | 平衡，73℉ | ASTM D-570 | 0.55 | % |
| 熔體流動(dòng)速率 | 標(biāo)稱(chēng),220℃/10.0kgf | ASTM D-1238 | 7.0 | g/10min | |
| 熔體流動(dòng)速率 | 標(biāo)稱(chēng),260℃/5.0kgf | ASTM D-1238 | 13.0 | g/10min | |
| 物理性能 | 比重 | 固體 | ASTM D-792 | 1.06 | |
| 模具收縮率 | flow,0.125" | ASTM D-955 | 5-7 | in/inE-3 | |
| 機(jī)械性能 | 抗拉屈服強(qiáng)度 | 2.0in/min | ASTM D-638 | 6000 | PSi |
| 抗拉斷裂強(qiáng)度 | 2.0in/min | ASTM D-638 | 5000 | PSi | |
| 拉伸斷裂伸長(zhǎng) | 2.0in/min | ASTM D-638 | 40.0 | % | |
| 拉伸模量 | 2.0in/min | ASTM D-638 | 260000 | PSi | |
| 撓曲屈服應(yīng)力 | 0.05in/min,2"span | ASTM D-790 | 8500 | PSi | |
| 撓曲模量 | 0.05in/min,2"span | ASTM D-790 | 260000 | PSi | |
| 洛氏硬度 | ASTM D-785 | 86 | R | ||
| 伊佐德缺口沖擊值 | 73℉ | ASTM D-256 | 6.0 | ft-lb/in | |
| 伊佐德缺口沖擊值 | -22℉ | ASTM D-256 | 1.1 | ft-lb/in | |
| 儀表控制抗沖擊總能量 | 73℉ | ASTM D-3763 | 225 | in-lbs | |
| 電氣性能 | 表面電阻率 | ASTM D-257 | >1E15 | ohm/sq | |
| 介電強(qiáng)度 | 油內(nèi)，125mils | ASTM D-149 | 406 | V/mil | |
| 介電常數(shù) | 50Hz | ASTM D-150 | 5.20 | ||
| 介電常數(shù) | 1MHz | ASTM D-150 | 3.21 | ||
| 損耗因數(shù) | 50Hz | ASTM D-150 | 0.1500 | ||
| 損耗因數(shù) | 1MHz | ASTM D-150 | 0.0260 | ||
| 熱性能 | 維卡軟化溫度 | B級(jí) | ASTM D-1525 | 211 | deg F |
| HDT | 66PSi,0.125",未退火 | ASTM D-1525 | 190 | deg F | |
| HDT | 66PSi,0.250",未退火 | ASTM D-1525 | 195 | deg F | |
| HDT | 264PSi,0.125",未退火 | ASTM D-1525 | 170 | deg F | |
| HDT | 264PSi,0.250",退火 | ASTM D-648 | 204 | deg F | |
| HDT | 264PSi,0.250",未退火 | ASTM D-648 | 175 | deg F | |
| CTE | -40℉-100℉ | ASTM D-831 | 4E-5 | in/in-F | |
| CTE | xflow,-40℉-100℉ | ASTM D-831 | 4E-5 | in/in-F | |
| CTE | flow,-22℉-32℉ | ASTM D-831 | 4E-5 | in/in-F | |
| CTE | flow,32℉-212℉ | ASTM D-831 | 5E-5 | in/in-F | |
| 光學(xué)性能 | 光澤度 | 無(wú)紋理，60度 | ASTM D-523 | 95 | |