產(chǎn)品參數(shù)
| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
| 物理性能 | 比重 | ASTM D72 | 1.41 | |||
| 吸水率 | ASTM D570 | 0.2 | % | |||
| 縮模率 | - | 平行方向 | 旭化成法 | 1.6-2.0 | % | |
| - | 垂直方向 | 旭化成法 | 1.6-2.0 | % | ||
| 機(jī)械性能 | 拉伸強(qiáng)度 | ASTM D638 | 61 | MPa | ||
| 延伸率 | ASTM D638 | 60 | % | |||
| 彎曲強(qiáng)度 | ASTM D790 | 88 | MPa | |||
| 彎曲模量 | ASTM D790 | 2600 | MPa | |||
| Izod缺口沖擊強(qiáng)度 | ASTM D256 | 59 | J/M | |||
| 洛氏硬度 | - | ASTM D785 | 80 | M | ||
| - | ASTM D785 | 115 | R | |||
| 磨耗 | ASTM D1044 | 14 | ||||
| 熱性能 | 熔融指數(shù) | ASTM D1238 | 9 | g/10min | ||
| 線(xiàn)膨脹系數(shù) | TMA法 | 10 | ||||
| 熱變形溫度 | - | 1.82MPa | ASTM D648 | 110 | ℃ | |
| - | 0.45MPa | ASTM D648 | 158 | ℃ | ||
| 阻燃性 | UL94 | HB | ||||