POM/日本旭化成/LA543 耐磨 擠出級 注塑級 工程原料
基本性能額定值單位測試方法
| 比重 | 1.38 | g/cm3 | ASTM D792, ISO 1183 |
| 熔體質(zhì)量流動速率 |
|
|
|
| 17 | g/10 min | ASTM D1238 |
| (190℃/2.16kg) | 17 | g/10 min | ISO 1133 |
| 成型收縮率 |
|
|
|
| (flow) | 1.8 to 2.2 | % | ASTM D955, ISO 294-4 |
| (Across flow) | 1.8 to 2.2 | % | ISO 294-4 |
| 吸水率 (24hr) | 0.30 | % | ASTM D570 |
| 洛氏硬度 |
|
| ASTM D785 |
| (M-Scale) | 81 |
|
|
| (R-Scale) | 120 |
|
|
機械性能額定值單位測試方法
| 拉伸模量 | 2800 | MPa | ISO 527-2 |
| 拉伸應(yīng)力 |
|
|
|
| (Yield) | 60.0 | MPa | ISO 527-2 |
| 57.0 | MPa | ASTM D638 |
| 拉伸伸長率 |
|
|
|
| (Break) | 30 | % | ASTM D638 |
| (Break) | 40 | % | ISO 527-2 |
| 彎曲模量 | 2650 | MPa | ASTM D790 |
| 彎曲強度 | 89.0 | MPa | ASTM D790 |
| 夏比缺口沖擊強度 (23°C) | 7.0 | kJ/m2 | ISO 179/1eA |
| IZOD缺口沖擊強度 | 69.0 | J/m | ASTM D256 |
熱性能額定值單位測試方法
| 熱畸變溫度 |
|
|
|
| (0.45MPa,未退火) | 165 | °C | ASTM D648, ISO 75-2/B |
| (1.8MPa,未退火) | 115 | °C | ASTM D648 |
| (1.8MPa,未退火) | 100 | °C | ISO 75-2/A |
| 線性熱膨脹系數(shù) (flow) | 0.00010 | cm/cm/°C | ASTM E831 |