Beta (?)-PPR? RA7050
聚丙烯無(wú)規(guī)共聚物
Borealis AG
產(chǎn)品說(shuō)明:
Beta-PPR? RA7050 is a PP-RCT(1), a Polypropylene-Random-Copolymer with an enhanced Crystalline structure brought about by a special ?-nucleation and with an improved Temperature resistance. Proof of the excellent performance characteristics of Beta-PPR? RA7050 is, for example, a categorised required strength (CRS) of 5 MPa at 70°C and 50 years in comparison to a value of 3.21 MPa for standard PP-R.
The colour of Beta-PPR? RA7050 is steel grey similar to RAL 7042.
In general Beta-PPR? RA7050 is intended to be used in applications for plumbing and heating, such as in-house hot and cold water pipes and fitiings, floor and wall heating systems and radiator connections.
添加劑 | · 成核劑 |
特性 | · 成核的· 耐熱性，中等· 無(wú)規(guī)共聚物
|
用途 | · 管道部件· 管道系統(tǒng)· 配件
|
外觀 | · 灰色 |
形式 | · 粒子 |
加工方法 | · 管路擠出成型· 擠出· 注射成型
|
物理性能 | 額定值 | 單位制 | 測(cè)試方法 |
密度 | 0.905 | g/cm3 | ISO 1183 |
熔流率（熔體流動(dòng)速率） (230°C/2.16 kg) | 0.30 | g/10 min | ISO 1133 |
機(jī)械性能 | 額定值 | 單位制 | 測(cè)試方法 |
拉伸模量 (注塑) | 900 | MPa | ISO 527-2/1 |
拉伸應(yīng)力 (屈服, 注塑) | 25.0 | MPa | ISO 527-2/50 |
拉伸應(yīng)變 (屈服, 注塑) | 10 | % | ISO 527-2/50 |
沖擊性能 | 額定值 | 單位制 | 測(cè)試方法 |
簡(jiǎn)支梁缺口沖擊強(qiáng)度 | ISO 179/1eA | ||
-20°C, 注塑 | 2.0 | kJ/m2 | |
0°C, 注塑 | 4.0 | kJ/m2 | |
23°C, 注塑 | 40 | kJ/m2 |
熱性能 | 額定值 | 單位制 | 測(cè)試方法 |
線形熱膨脹系數(shù) - 流動(dòng) (0 到 70°C) | 1.5E-4 | cm/cm/°C | DIN 53752 |
導(dǎo)熱系數(shù) | 0.24 | W/m/K | DIN 52612 |
電氣性能 | 額定值 | 單位制 | 測(cè)試方法 |
表面電阻率 | > 1.0E+12 | ohms | DIN 53482/VDE 0303 |
注射 | 額定值 | 單位制 | |
料斗溫度 | 200 | °C | |
射嘴溫度 | 220 到 250 | °C | |
加工（熔體）溫度 | < 250 | °C | |
擠出 | 額定值 | 單位制 | |
料筒1區(qū)溫度 | 215 到 230 | °C | |
料筒2區(qū)溫度 | 215 到 230 | °C | |
料筒3區(qū)溫度 | 215 到 230 | °C | |
料筒4區(qū)溫度 | 215 到 230 | °C | |
料筒5區(qū)溫度 | 215 到 230 | °C | |
接頭溫度 | 220 到 230 | °C | |
熔體溫度 | 220 到 230 | °C | |
口模溫度 | 220 到 230 | °C | |
擠壓說(shuō)明 | |||
Screen pack: Sieve 60 to 100 mesh | |||